Polyol and ISO, Polyether, PU Chemical for Shoe Sole manufacturer / supplier in China, offering Polyether Resin for Insole, Polyurethane Raw Material for Slipper/Sandals, Polyurethane Resin and so on.

(/ )

Polyether Resin for Insole

FOB Price: Get Latest Price
Min. Order: 1 Ton
Production Capacity: 150000ton/Year
Transport Package: Steel Drum
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 1005A/5305B
  • Natural Resin: Rosin
  • Polyol and ISO: PU Chemical for Shoe Sole
  • Specification: polyol in 220kg/drum; iso in 235kg/drum
  • HS Code: 3909500000
  • Synthetic Resin: Polyurethane Resin
  • Color: Transparent
  • Trademark: headspring
  • Origin: China
Product Description
A-1005A/B-5305
:,,,
Characteristic: Low density, good handle and surface, good dimension stability
:
Application: Polyether Insole
Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40ºC)

Density (g·cm-3/40ºC)

Package(kg)
A-1005A
cream white liquid
500~8001.01~1.0218
B-5305
Yellowish Transparent liquid or waxy
300~6001.08~1.220
 Materials preheat
A-1001A:  50~60ºC2~4     preheated at 50~60ºC for 2~4 hours          
B-5301:   60~70ºC10~15   preheated at 60~70ºC for 10~15 hours
Typical processing parameters & Reaction parameter

 
Items

A/B Materials Temperatures
(ºC)

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature(ºC)
Demold Time(min)

Parameter
30~35/35~40100/45~477~950~600.13~0.1645~553~5
Catalyst380g±20g/18kg      The adding content of Catalyst should be 380g±20g/18kg
0~90g/18kg         The adding content of water should be 0~90g/18kg according to the reality
0~600g/18kg    The adding content of water should be 0~600g/18kg according to the reality
Physical properties 

Items

Molded Density (g/cm3)

Hardness
(Shore C )

Tensile strength
(MPa)

Elongation (%)

Tear Strength
(kN/m)
 
168, 70ºC,95%
168h, 70ºC, 95%r.h. hydrolysis
 strength retention(%)

Physical properties
0.28~0.5028~502.0~5.0300~38018~26>90
.
Demold time may be prolonged with the increase of sole thickness
6mm
These physical data are acquired by testing a sample of 6mm thick.
 
,.
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
(,).
Free foam density will vary with the seasons (temperature, humidity).
.
Stripping time will be extended with the increase of the thickness of moldings.
: 90,80/min*4.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
 ,.,.
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
 
 
 
 
 

Polyether Resin for Insole
Polyether Resin for Insole
 
Send your message to this supplier
Avatar
Miss vicky
*From:
To: Miss vicky
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category