Polyurethane System for Footwear, Polyol Isocyanate for Shoe Sole, Polyurethane for Shoe Sole manufacturer / supplier in China, offering Headspring PU Two-Component Resin for Safety Shoe Sole: Polyol and ISO, Polyurethane Chemical for Man Lather Outsole, Headspring PU Prepolymer/PU Chemical /PU Prepolymer PU Two-Component Raw Material for (flexible foam) Shoe Sole: Polyol and ISO and so on.

(/ )

Supplier Homepage Product SAFETY SHOE SOLE MATERIAL Headspring PU Two-Component Resin for Safety Shoe Sole: Polyol and ISO

Headspring PU Two-Component Resin for Safety Shoe Sole: Polyol and ISO

FOB Price: US $1.85 / kg
Min. Order: 500 kg
Min. Order FOB Price
500 kg US $1.85/ kg
Get Latest Price
Port: Ningbo, China
Production Capacity: 150000 Tons/Year
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 6570/7118
  • Polyol Appearance: Yellow Transparent or White Liquid
  • Polyol Viscosity: 0.35-0.65 PA . S
  • Polyol Density: 1.16-1.20
  • Polyol Package: 18 Kg/Can or 220 Kg/Drum
  • Trademark: Headspring
  • Specification: ISO9001; ISO14001
  • HS Code: 39079999
  • Synthetic Resin: Polyurethane Resin
  • Isocyanate Appearance: Transparent Liquid
  • Isocyanate Viscosity: 0.05-0.20 PA . S
  • Isocyanate Density: 1.18-1.20
  • Isocyanate: 20kg/Can or 235 Kg/Drum
  • Transport Package: 18 Kg, 20 Kg, 220kg, 235 Kg
  • Origin: Wenling Zhejiang
Product Description
 
Shop sign: ZG-P-6570/ZG-I-7118
Dual density PU Resin for labor protection shoes (safety shoe) sole
1. Characteristic: Medium and low hardness, medium and high density.
2. Characteristic: Applicable to the production of single density or double density safety shoes
3. Typical properties of PU Resin
Name of productsAppearanceViscosity
(Pa·s/50ºC)
Density
(g/cm3/40ºC)
Package
(kg)
ZG-P-6570White or pale yellow, liquid, no foreign material0.50-0.801.16-1.2018
ZG-I-7118Transparent liquid, no foreign material0.20-0.401.18-1.2020
Reference shipments ratio: A/B=30/24 (barrel)
4. Catalysts and auxiliary agents:
   outsole:ZG-P-6570/ZG-AC-2/water/hardner=18kg/280g/10-20g/0-400g(Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions. )
   midsole:ZG-P-6570/ZG-AC-2/water/hardner=18kg/280g/65~85g/0~800g(Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions. )
5. ( Molding conditions & physical properties):
ReactivityTechnical indexTest itemReference physical properties
Reference ratio
P+C/I  
outsole:100/68-70 
Molded density of sole
(g/cm3)
Outsole:0.90-1.10
midsole:100/82-84midsole:0.45-0.55
Using temperature(ºC)A material: 45-50; B material:38-42Hardness (type A)outsole: 55~75
midsole: 40~55
Cream time(s)6~9Tensile strength(MPa)600~700
Rise time(s)25~35Elongation(%)5.0~7.0
Metal mold temperature
(ºC)
45~55NBS abrasion resistance(%)10%
Demould time
(min)
3.0~6.0Free foam density
(g/cm3)
outsole:0.60~0.70
midsole:0.28-0.34
  Folding endurance (room temperature)
(40,000 gap length, mm)
<8
 
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
Send your message to this supplier
Avatar
Miss Nina
*From:
To: Miss Nina
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category