Polyurethane Raw Matreial manufacturer / supplier in China, offering PU Chemical for Sandals, Polyurethane Raw Material for Slipper/Sandals, Polyurethane Resin and so on.

(/ )

Supplier Homepage Product SANDAL SHOE SOLE PU Chemical for Sandals

PU Chemical for Sandals

FOB Price: US $1,650 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $1,650/ Ton
Get Latest Price
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 5005/5320
  • Polyol Isocaynate: Shoe Sole Chemical
Product Description
( Shop sign): ZG-P-5005/ZG-I-5320

Medium and high-density PU Resin for shoe sole with the upper
1. :,
Characteristic: Medium and low hardness, medium and high density
2. :
Application: Applicable to the production of shoe sole with the upper for men and women
3. Typical properties of PU Resin

   
Name of products
   
Appearance
   
Viscosity
(Pa·s/50ºC)
   
Density
(g/cm3/40ºC)
  
Package
(kg)
ZG-P-5005,
White or pale yellow, liquid, no foreign material
0.50-0.801.16-1.2018
ZG-I-5320
Transparent liquid, no foreign material
0.20-0.401.18-1.2020
(Reference shipments ratio):A/B=30/25()
Reference shipments ratio: A/B=30/25 (barrel)
4. Catalysts and auxiliary agents:
   ZG-P-5005/ZG-AC-2/ =18kg/235g/0-30g :.
   ZG-P-5005/ZG-AC-2/water =18kg/235g/0-30g   Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):


Reactivity

Technical index

Test item

Reference physical properties

Reference ratio
P+C/I  
100/83-85
Molded density of sole
(g/cm3)
0.55~0.60

Material temperature(ºC)
A:45-50;B:38-42
A material: 45-50; B material:38-42
(A)
Hardness (type A)
40~50

Cream time(s)
7~9
Tensile strength(MPa)
6.0~8.0

Rise time(s)
30~45
Elongation(%)
350~450

Metal mold temperature
(ºC)
45~55NBS
NBS abrasion resistance(%)
10%

Demould time
(min)
3.0~5.0
Free foam density
(g/cm3)
0.25~0.30
  ()
(4,mm)
Folding endurance (room temperature)
(40,000 gap length mm)
<8
 
,.
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
(,).
Free foam density will vary with the seasons (temperature, humidity).
.
Stripping time will be extended with the increase of the thickness of moldings.
: 90,80/min*4.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

PU Chemical for Sandals
PU Chemical for Sandals
    Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
Send your message to this supplier
Avatar
Miss vicky
*From:
To: Miss vicky
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category