Polyurethane System for Footwear, Polyol Isocyanate for Shoe Sole, Polyurethane for Shoe Sole manufacturer / supplier in China, offering PU Resin for Safety Shoe Sole, Polyurethane Raw Material for Slipper/Sandals, Polyurethane Resin and so on.

(/ )

Supplier Homepage Product SAFETY SHOE SOLE MATERIAL PU Resin for Safety Shoe Sole

PU Resin for Safety Shoe Sole

FOB Price: US $1.5 / kg
Min. Order: 500 kg
Min. Order FOB Price
500 kg US $1.5/ kg
Get Latest Price
Production Capacity: 150000 Tons/Year
Transport Package: 18 Kg, 20 Kg, 220kg, 235 Kg
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: ZH6570/ZH5002
  • Polyol Appearance: Yellow Transparent or White Liquid
  • Polyol Viscosity: 0.35-0.65 PA . S
  • Polyol Density: 1.16-1.20
  • Polyol Package: 18 Kg/Can or 220 Kg/Drum
  • Trademark: Headspring
  • Origin: Wenling Zhejiang
  • Synthetic Resin: Polyurethane Resin
  • Isocyanate Appearance: Transparent Liquid
  • Isocyanate Viscosity: 0.05-0.20 PA . S
  • Isocyanate Density: 1.18-1.20
  • Isocyanate: 20kg/Can or 235 Kg/Drum
  • Specification: ISO9001; ISO14001
  • HS Code: 39095000
Product Description

PU Resin for Safety Shoe Sole
ZH6570/ZH5002
Dual density PU Resin for labor protection shoes (safety shoe) sole
1.Characteristic: Medium and low hardness, medium and high density.
2.Characteristic: Applicable to the production of single density or double density safety shoes
3. Typical properties of PU Resin
  
Name of products
  
Appearance
  
Viscosity
(Pa·s/50ºC)
  
Density
(g/cm3/40ºC)
 
Package
(kg)
ZH6570,
White or pale yellow, liquid, no foreign material
0.50-0.801.16-1.20220
ZH5002
Transparent liquid, no foreign material
0.20-0.401.18-1.20235
(Reference shipments ratio):POL/ISO=45/35()
Reference shipments ratio: POL/ISO=45/35 (Drum)
4. Catalysts and auxiliary agents:
ZH6570/ZH1001/Water/ZH1002=220kg/3.5kg/150 g/2kg:.
(uxiliary agent joined in different areas and different environments and production conditions adjusted accordingly.) ZH6570/ZH1001/Water/ZH1002=220kg/3.5kg/700 g/0 kg::.
(uxiliary agent joined in different areas and different environments and production conditions adjusted accordingly.)
5. (Typical processing parameters& Typcal properties):

Reaction characteristics

technical standards

Test item

Physical properties

Reference ratio
P+C/I  
:100/68-70
Molded density
(g/cm3)
:0.80-1.0
:100/82-84:0.45-0.55

Material temperature(ºC)
A:45-50;B:38-42(A)
Hardness(type A)
:  55~75
:  40~55

Cream time(s)
6~9
Tensile strength(MPa)
600~700

End of Rise time(s)
25~35
Elingation(%)
5.0~7.0

Metal mold temperature
(ºC)
45~55NBS
Wear(%)
10%

Demould time
(min)
3.0~6.0
Free rise foam density
(g/cm3)
:0.60~.70
:0.28-0.34


()
(4,mm)
Folding(room temperature)
(40,000 gap length mm)
<8
 
,.
With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.
(,).
the free foam density according to the seasons (temperature, humidity) vary
.
Ejection time with the increase of the thickness of molded extension
: 90,80/min*4.
Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million
 ,.,.
Data listed above are just for reference .The detail data are subjected to practical operation.If other requests for physical properties,please contact us.

Send your message to this supplier
Avatar
Mr. peter
*From:
To: Mr. peter
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category