Polyurethane for Men and Women Shoe Sole Zg-P-5001/Zg-I-5002
|FOB Price:||US $2.1 / kilogram|
|Min. Order:||18 Tons|
|Min. Order||FOB Price|
|18 Tons||US $2.1/ kilogram|
|Production Capacity:||150, 000 Tons/Year|
|Transport Package:||Polyol: 220kg/Drum, ISO: 235kg/Drum, 18000kg/20′gp|
|Payment Terms:||L/C, T/T|
- Model NO.: ZG-P-5001/ZG-I-5002
- Color: White
- Origin: Zhejiang, China
- Synthetic Resin: Polyurethane Resin
- Trademark: headspring
High-hardness and medium and high-density shoe sole PU Resin
1. Characteristic: High hardness, medium and high density.
2. Application: Applicable to the production of soles for men and women.
-Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
--Free foam density will vary with the seasons (temperature, humidity).
--Stripping time will be extended with the increase of the thickness of moldings.
--Folding endurance conditions: Bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
--Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
|Name of products||Appearance||Viscosity|
( Pa @ s/50 °C)
( g/cm 3 /40 °C)
( kg )
|ZG-P-5001||White or pale yellow, liquid, no foreign material||0.40 -0.90||1.16-1.19||18|
|ZG-I-5002||Transparent liquid and no foreign material||0.20-0.40||1.18-1.20||20|
Reference shipments ratio: A/B=25/28 (barrel)
4. Catalysts and auxiliary agents :
ZG-P-5001 /ZG-AC-2 =18kg/220g Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. Molding conditions & physical properties :
|Reactivity||Technical index||Test item||Reference physical properties|
|100/119-121||Molded density of sole|
( g/cm 3 )
|Using temperature(°C)||A material: 45-50; B material:38-42||Hardness (type A)||60~70|
|Cream time(s)||7~9||Tensile strength(MPa)||6.0~8.0|
|Metal mold temperature|
|45~55||NBS abrasion resistance(%)||≥ 10%|
( min )
|1.5~3.0||Free foam density|
( g/cm 3 )
|Folding endurance (room temperature)|
(40,000 gap length, mm)