PU Resin for Insole, Polyol Isocyanate for Shoe Sole, Polyurethane for Shoe Sole manufacturer / supplier in China, offering Polyurethane Resin for Insole, Polyurethane Chemical for Man Lather Outsole, Headspring PU Prepolymer/PU Chemical /PU Prepolymer PU Two-Component Raw Material for (flexible foam) Shoe Sole: Polyol and ISO and so on.

(/ )

Supplier Homepage Product INSOLE MATERIAL Polyurethane Resin for Insole

Polyurethane Resin for Insole

FOB Price: US $1.7 / kg
Min. Order: 500 kg
Min. Order FOB Price
500 kg US $1.7/ kg
Get Latest Price
Port: Ningbo, China
Production Capacity: 150000 Tons/Year
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Product Catalog
E-Catalog
7 Products
Content
Product Image
Product Name
FOB Price
Port
Basic Info
  • Model NO.: ZH8590/ZH9690
  • Polyol Appearance: Yellow Transparent or White Liquid
  • Polyol Viscosity: 0.35-0.65 PA . S
  • Polyol Density: 1.16-1.20
  • Polyol Package: 18 Kg/Can or 220 Kg/Drum
  • Trademark: Headspring
  • Specification: ISO9001; ISO14001
  • HS Code: 39095000
  • Synthetic Resin: Polyurethane Resin
  • Isocyanate Appearance: Transparent Liquid
  • Isocyanate Viscosity: 0.05-0.20 PA . S
  • Isocyanate Density: 1.18-1.20
  • Isocyanate: 20kg/Can or 235 Kg/Drum
  • Transport Package: 18 Kg, 20 Kg, 220kg, 235 Kg
  • Origin: Wenling Zhejiang
Product Description

Polyurethane Resin for Insole
 A-100
5A/B-5305
:,,,
Characteristic: Low density, good handle and surface, good dimension stability
:
Application: Polyether Insole
Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPs/40ºC)

Density (g·cm-3/40ºC)

Package(kg)
A-1005A
cream white liquid
500~8001.01~1.0218
B-5305
Yellowish Transparent liquid or waxy
300~6001.08~1.220
 Materials preheat
A-1001A:  50~60ºC2~4     preheated at 50~60ºC for 2~4 hours          
B-5301:   60~70ºC10~15   preheated at 60~70ºC for 10~15 hours
Typical processing parameters & Reaction parameter

 
Items

A/B Materials Temperatures
(ºC)

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature(ºC)
Demold Time(min)

Parameter
30~35/35~40100/45~477~950~600.13~0.1645~553~5
Catalyst380g±20g/18kg      The adding content of Catalyst should be 380g±20g/18kg
0~90g/18kg         The adding content of water should be 0~90g/18kg according to the reality
0~600g/18kg    The adding content of water should be 0~600g/18kg according to the reality
Physical properties 

Items

Molded Density (g/cm3)

Hardness
(Shore C )

Tensile strength
(MPa)

Elongation (%)

Tear Strength
(kN/m)
 
168, 70ºC,95%
168h, 70ºC, 95%r.h. hydrolysis
 strength retention(%)

Physical properties
0.28~0.5028~502.0~5.0300~38018~26>90
.
Demold time may be prolonged with the increase of sole thickness
6mm
These physical data are acquired by testing a sample of 6mm thick.
 
,.
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
(,).
Free foam density will vary with the seasons (temperature, humidity).
.
Stripping time will be extended with the increase of the thickness of moldings.
: 90,80/min*4.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
 ,.,.
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
 
Send your message to this supplier
Avatar
Mr. hengtaiyuan
*From:
To: Mr. hengtaiyuan
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category