Safety Shoes Material manufacturer / supplier in China, offering Polyol and Isocaynate for Safety Shoes, PU Foam Chemical/Polyurethane Resin for Lady Footwear, High-Heeled Shoe Sole a-5090/B-5320, Polyurethane Resin for Work Shoe Sole a-5005/B-5002 and so on.

(/ )

Supplier Homepage Product SAFETY SHOE SOLE MATERIAL Polyol and Isocaynate for Safety Shoes

Polyol and Isocaynate for Safety Shoes

FOB Price: US $1,900 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $1,900/ Ton
Get Latest Price
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 6570/5002
  • Polyster Resin: Dule Component
Product Description
( Shop sign): ZG-P-6570/ZG-I-5002

Dual density PU Resin for labor protection shoes (safety shoe) sole
1. :,
Characteristic: Medium and low hardness, medium and high density.
2. :.
Characteristic: Applicable to the production of single density or double density safety shoes
3. Typical properties of PU Resin

   
Name of products
   
Appearance
   
Viscosity
(Pa·s/50ºC)
   
Density
(g/cm3/40ºC)
  
Package
(kg)
ZG-P-6570,
White or pale yellow, liquid, no foreign material
0.50-0.801.16-1.2018
ZG-I-5002
Transparent liquid, no foreign material
0.20-0.401.18-1.2020
(Reference shipments ratio):A/B=30/24()
Reference shipments ratio: A/B=30/24 (barrel)
4. Catalysts and auxiliary agents:
   ZG-P-6570/ZG-AC-2//=18kg/280g/10~20g/0~400 g:. 
(uxiliary agent joined in different areas and different environments and production conditions adjusted accordingly.) 
ZG-P-6570/ZG-AC-2//=18kg/280g/65~85g/0~800g::.
(uxiliary agent joined in different areas and different environments and production conditions adjusted accordingly.) 
5. (Typical processing parameters& Typcal properties):


Reaction characteristics

technical standards

Test item

Physical properties

Reference ratio
P+C/I  
:100/68-70
Molded density
(g/cm3)
:0.90-1.10
:100/82-84:0.45-0.55

Material temperature(ºC)
A:45-50;B:38-42(A)
Hardness(type A)
:  55~75
:  40~55

Cream time(s)
6~9
Tensile strength(MPa)
600~700

End of Rise time(s)
25~35
Elingation(%)
5.0~7.0

Metal mold temperature
(ºC)
45~55NBS
Wear(%)
10%

Demould time
(min)
3.0~6.0
Free rise foam density
(g/cm3)
:0.60~.70
:0.28-0.34
  ()
(4,mm)
Folding(room temperature)
(40,000 gap length mm)
<8
 
,.
With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.
(,).
the free foam density according to the seasons (temperature, humidity) vary
.
Ejection time with the increase of the thickness of molded extension
: 90,80/min*4.
Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million

  • ,.,.
Data listed above are just for reference .The detail data are subjected to practical operation.If other requests for physical properties,please contact us.
Polyol and Isocaynate for Safety Shoes

Send your message to this supplier
Avatar
Miss vicky
*From:
To: Miss vicky
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category