Polyurethane for Shoe Sole, Flexible PU Foam Outsole manufacturer / supplier in China, offering High-Hardness and Medium and High-Density PU Resin for Shoe Sole of Woman High-Heeled Shoes Zg-P-5090/Zg-I-5320, Polyurethane Resin for Work Shoe Sole a-5005/B-5002, PU Resin for Auto Parts Zg-P-3650s/Zg-I-9823 and so on.

(/ )

Supplier Homepage Product HIGH HEELED SHOE SOLE MATERIAL High-Hardness and Medium and High-Density PU Resin for Shoe Sole of Woman High-Heeled Shoes Zg-P-5090/Zg-I-5320

High-Hardness and Medium and High-Density PU Resin for Shoe Sole of Woman High-Heeled Shoes Zg-P-5090/Zg-I-5320

FOB Price: Get Latest Price
Min. Order: 18 Tons
Production Capacity: 150000 Tons
Transport Package: Polyol: 220kg/Drum, ISO: 235kg/Drum, 18000kg/20′gp
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: ZG-P-5090/ZG-I-5320
  • Color: White
  • Origin: Zhejiang, China
  • Synthetic Resin: Polyurethane Resin
  • Trademark: Headspring
  • HS Code: 3909500000
Product Description
( Shop sign): ZG-P-5090/ZG-I-5320
,
High-hardness and medium and high-density PU Resin for shoe sole of woman high-heeled shoes
1.
Characteristic: High hardness, medium and high density
2.
Application: Applicable to the production of female high-heeled shoes
3. Typical properties of PU Resin
  
Name of products
  
Appearance
  
Viscosity
(Pa·s/50ºC)
  
Density
(g/cm3/40ºC)
 
Package
(kg)
ZG-P-5090,
White or pale yellow, liquid, no foreign material
0.40-0.801.16-1.2018
ZG-I-5320
Transparent liquid, no foreign material
0.10-0.301.18-1.2020

 
(Reference shipments ratio):A/B=25/28()
Reference shipments ratio: A/B=25/28 (barrel)
4. Catalysts and auxiliary agents:
   ZG-P-5090/ZG-AC-2/ =18kg/220g/40-80g:.
   ZG-P-5090/ZG-AC-2/water =18kg/220g/40-80g   Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):

Reactivity

Technical index

Test item

Reference physical properties

Reference ratio
P+C/I 
100/118-122
Molded density of sole
(g/cm3)
0.55~0.75

Using temperature(ºC)
A:45-50;B:38-42 A material: 45-50; B material:38-42(A)
Hardness (type A)
75~85

Cream time(s)
6~9
Tensile strength(MPa)
3.5~4.5

Rise time(s)
30~45
Elongation(%)
250~350

Metal mold temperature
(ºC)
45~55NBS
NBS abrasion resistance(%)
≥10%

Demould time
(min)
5.0~7.0
Free foam density
(g/cm3)
0.28~0.35


()
(4,mm)
Folding endurance (room temperature)
(40,000 gap length mm)
<8
 

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.

Send your message to this supplier
Avatar
Miss Amy
*From:
To: Miss Amy
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category