Polyol Price, Polyurethane Resin for Shoe Sole, Polyols and Isocyanates manufacturer / supplier in China, offering Polyol Isocyanate Soft, Polyurethane Raw Material for Slipper/Sandals, Polyurethane Resin and so on.

(/ )

Supplier Homepage Product SANDAL SHOE SOLE Polyol Isocyanate Soft

Polyol Isocyanate Soft

FOB Price: US $1.6-2.1 / kilogram
Min. Order: 500 kilogram
Min. Order FOB Price
500 kilogram US $1.6-2.1/ kilogram
Get Latest Price
Production Capacity: 150000 Ton/Year
Transport Package: Drum
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 7165/7249
  • Natural Resin: PU Resin
  • Color: White
  • Specification: 220kg/drum&235kg/drum
  • HS Code: 3909500000
  • Synthetic Resin: Polyurethane Resin
  • Characteristic: Prepolymer
  • Trademark: Headspring
  • Origin: China
Product Description

(Shop sign): ZG-P-7165/ZG-I-7249
,
Medium and low-hardness and medium and low-density PU Resin for sole of casual shoes for both men and women
1. :,.
Characteristic: Medium and low hardness, medium and  low density.
2. :.
Application: Applicable to the production of medium soles of casual shoes for both men and women
3. Typical properties of PU Resin

  
Name of products
  
Appearance
  
Viscosity
(Pa·s/50ºC)
  
Density
(g/cm3/40ºC)
 
Package
(kg)
ZG-P-7165,
White or pale yellow, liquid, no foreign material
0.50-1.001.16-1.2018
ZG-I-7249
Transparent liquid, no foreign material
0.10-0.301.18-1.20 
Reference shipments ratio: A/B=30/23(barrel)
4. Catalyst and auxiliary agents .
ZG-P-7165/ZG-AC-2/water =18kg/220g/60-80g  Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):

Reactivity

Technical index

Test item

Reference physical properties

Reference ratio
P+C/I  
100/87-89
Molded density of sole
(g/cm3)
0.38~0.45

Using temperature(ºC)

A material: 45-50; B material:38-42

Hardness (type A)
40~55

Cream time(s)
6~9
Tensile strength(MPa)
3.5~4.5

Rise time(s)
30~45
Elongation(%)
350~450

Metal mold temperature
(ºC)
55~65
NBS abrasion resistance(%)
10%

Demould time
(min)
4.0~6.0
Free foam density
(g/cm3)
0.15~0.18
  
Folding endurance (room temperature)
(40,000 gap length mm)
<8
 
,.
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added..
Free foam density will vary with the seasons (temperature, humidity).
.
Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

 

Polyol Isocyanate Soft

--Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

--Free foam density will vary with the seasons (temperature, humidity).

--Stripping time will be extended with the increase of the thickness of moldings.

--Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

--Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.


Polyol Isocyanate Soft

You Might Also Like
Send your message to this supplier
Avatar
Miss vicky
*From:
To: Miss vicky
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category